Grade 32 Titanium vs. Grade Ti-Pd7B Titanium

Both grade 32 titanium and grade Ti-Pd7B titanium are titanium alloys. They have a moderately high 91% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade 32 titanium and the bottom bar is grade Ti-Pd7B titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 11
17
Fatigue Strength, MPa 390
200
Poisson's Ratio 0.32
0.32
Shear Modulus, GPa 40
40
Tensile Strength: Ultimate (UTS), MPa 770
390
Tensile Strength: Yield (Proof), MPa 670
310

Thermal Properties

Latent Heat of Fusion, J/g 410
420
Maximum Temperature: Mechanical, °C 310
320
Melting Completion (Liquidus), °C 1610
1660
Melting Onset (Solidus), °C 1560
1610
Specific Heat Capacity, J/kg-K 550
540
Thermal Conductivity, W/m-K 7.5
22
Thermal Expansion, µm/m-K 8.2
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
7.1

Otherwise Unclassified Properties

Density, g/cm3 4.5
4.5
Embodied Carbon, kg CO2/kg material 32
49
Embodied Energy, MJ/kg 530
840
Embodied Water, L/kg 180
520

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
62
Resilience: Unit (Modulus of Resilience), kJ/m3 2100
440
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 35
35
Strength to Weight: Axial, points 47
24
Strength to Weight: Bending, points 41
26
Thermal Diffusivity, mm2/s 3.0
8.9
Thermal Shock Resistance, points 63
30

Alloy Composition

Aluminum (Al), % 4.5 to 5.5
0
Carbon (C), % 0 to 0.080
0 to 0.1
Hydrogen (H), % 0 to 0.015
0 to 0.015
Iron (Fe), % 0 to 0.25
0 to 0.2
Molybdenum (Mo), % 0.6 to 1.2
0
Nickel (Ni), % 0
0 to 0.050
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.11
0 to 0.4
Palladium (Pd), % 0
0.12 to 0.3
Silicon (Si), % 0.060 to 0.14
0
Tin (Sn), % 0.6 to 1.4
0
Titanium (Ti), % 88.1 to 93
98.8 to 99.9
Vanadium (V), % 0.6 to 1.4
0
Zirconium (Zr), % 0.6 to 1.4
0
Residuals, % 0 to 0.4
0 to 0.4