Grade 36 Titanium vs. C41300 Brass
Grade 36 titanium belongs to the titanium alloys classification, while C41300 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade 36 titanium and the bottom bar is C41300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 11 | |
| 2.0 to 44 |
| Poisson's Ratio | 0.36 | |
| 0.33 |
| Shear Modulus, GPa | 39 | |
| 42 |
| Shear Strength, MPa | 320 | |
| 230 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 530 | |
| 300 to 630 |
| Tensile Strength: Yield (Proof), MPa | 520 | |
| 120 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 180 |
| Melting Completion (Liquidus), °C | 2020 | |
| 1040 |
| Melting Onset (Solidus), °C | 1950 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 380 |
| Thermal Expansion, µm/m-K | 8.1 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.3 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 58 | |
| 2.7 |
| Embodied Energy, MJ/kg | 920 | |
| 44 |
| Embodied Water, L/kg | 130 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1260 | |
| 69 to 1440 |
| Stiffness to Weight: Axial, points | 9.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 23 | |
| 9.6 to 20 |
| Strength to Weight: Bending, points | 23 | |
| 11 to 19 |
| Thermal Shock Resistance, points | 45 | |
| 11 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Copper (Cu), % | 0 | |
| 89 to 93 |
| Hydrogen (H), % | 0 to 0.0035 | |
| 0 |
| Iron (Fe), % | 0 to 0.030 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Niobium (Nb), % | 42 to 47 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.16 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.7 to 1.3 |
| Titanium (Ti), % | 52.3 to 58 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 5.1 to 10.3 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |