Grade 360 Molybdenum vs. EN 1.4923 Stainless Steel
Grade 360 molybdenum belongs to the otherwise unclassified metals classification, while EN 1.4923 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 360 molybdenum and the bottom bar is EN 1.4923 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 190 |
| Elongation at Break, % | 6.3 to 17 | |
| 12 to 21 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 120 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 620 | |
| 870 to 980 |
| Tensile Strength: Yield (Proof), MPa | 270 to 530 | |
| 470 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 480 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 2.9 |
| Embodied Energy, MJ/kg | 330 | |
| 41 |
| Embodied Water, L/kg | 360 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 37 to 64 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 450 | |
| 570 to 1580 |
| Stiffness to Weight: Axial, points | 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 17 | |
| 31 to 35 |
| Strength to Weight: Bending, points | 12 to 16 | |
| 26 to 28 |
| Thermal Shock Resistance, points | 14 to 21 | |
| 30 to 34 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0.18 to 0.24 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 83.5 to 87.1 |
| Manganese (Mn), % | 0 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 99.9 to 100 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0.3 to 0.8 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |