Grade 360 Molybdenum vs. EN AC-46600 Aluminum
Grade 360 molybdenum belongs to the otherwise unclassified metals classification, while EN AC-46600 aluminum belongs to the aluminum alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 360 molybdenum and the bottom bar is EN AC-46600 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 72 |
| Elongation at Break, % | 6.3 to 17 | |
| 1.1 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 120 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 620 | |
| 180 |
| Tensile Strength: Yield (Proof), MPa | 270 to 530 | |
| 110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 490 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 890 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 7.8 |
| Embodied Energy, MJ/kg | 330 | |
| 150 |
| Embodied Water, L/kg | 360 | |
| 1080 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 37 to 64 | |
| 1.7 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 450 | |
| 81 |
| Stiffness to Weight: Axial, points | 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 50 |
| Strength to Weight: Axial, points | 12 to 17 | |
| 18 |
| Strength to Weight: Bending, points | 12 to 16 | |
| 25 |
| Thermal Shock Resistance, points | 14 to 21 | |
| 8.1 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 85.6 to 92.4 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Copper (Cu), % | 0 | |
| 1.5 to 2.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.8 |
| Lead (Pb), % | 0 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.35 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.65 |
| Molybdenum (Mo), % | 99.9 to 100 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 to 0.35 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 6.0 to 8.0 |
| Tin (Sn), % | 0 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.15 |