Grade 361 Molybdenum vs. Solder Alloy 142

Both grade 361 molybdenum and solder alloy 142 are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade 361 molybdenum and the bottom bar is solder alloy 142.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 310
33
Elongation at Break, % 6.3
37
Poisson's Ratio 0.31
0.4
Shear Modulus, GPa 120
12
Tensile Strength: Ultimate (UTS), MPa 620
43

Thermal Properties

Latent Heat of Fusion, J/g 370
42
Specific Heat Capacity, J/kg-K 250
170
Thermal Expansion, µm/m-K 7.0
25

Otherwise Unclassified Properties

Density, g/cm3 10
9.3
Embodied Carbon, kg CO2/kg material 28
9.4
Embodied Energy, MJ/kg 330
160
Embodied Water, L/kg 360
890

Common Calculations

Stiffness to Weight: Axial, points 17
2.0
Stiffness to Weight: Bending, points 22
11
Strength to Weight: Axial, points 17
1.3
Strength to Weight: Bending, points 16
2.9
Thermal Shock Resistance, points 21
3.7

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
2.5 to 3.5
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.010
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.010
0 to 0.020
Lead (Pb), % 0
47.4 to 50
Molybdenum (Mo), % 99.9 to 100
0
Nickel (Ni), % 0 to 0.0050
0 to 0.010
Nitrogen (N), % 0 to 0.0020
0
Oxygen (O), % 0 to 0.0070
0
Silicon (Si), % 0 to 0.010
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
47.5 to 48.5
Zinc (Zn), % 0
0 to 0.0010