Grade 363 Molybdenum vs. EN 1.4313 Stainless Steel
Grade 363 molybdenum belongs to the otherwise unclassified metals classification, while EN 1.4313 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is grade 363 molybdenum and the bottom bar is EN 1.4313 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 200 |
| Elongation at Break, % | 6.2 to 11 | |
| 12 to 17 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 120 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 720 | |
| 750 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 350 to 620 | |
| 580 to 910 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 480 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 2.4 |
| Embodied Energy, MJ/kg | 330 | |
| 34 |
| Embodied Water, L/kg | 360 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 57 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 630 | |
| 870 to 2100 |
| Stiffness to Weight: Axial, points | 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 27 to 36 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 23 to 28 |
| Thermal Shock Resistance, points | 19 to 24 | |
| 27 to 36 |
Alloy Composition
| Carbon (C), % | 0.010 to 0.030 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 12 to 14 |
| Iron (Fe), % | 0 to 0.010 | |
| 78.5 to 84.2 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 99.3 to 99.5 | |
| 0.3 to 0.7 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 to 0.020 |
| Oxygen (O), % | 0 to 0.0030 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0.4 to 0.55 | |
| 0 |
| Zirconium (Zr), % | 0.060 to 0.12 | |
| 0 |