Grade 363 Molybdenum vs. SAE-AISI D4 Steel
Grade 363 molybdenum belongs to the otherwise unclassified metals classification, while SAE-AISI D4 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 363 molybdenum and the bottom bar is SAE-AISI D4 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 190 |
| Elongation at Break, % | 6.2 to 11 | |
| 8.4 to 15 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 120 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 720 | |
| 760 to 2060 |
| Tensile Strength: Yield (Proof), MPa | 350 to 620 | |
| 470 to 1540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 480 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 3.3 |
| Embodied Energy, MJ/kg | 330 | |
| 49 |
| Embodied Water, L/kg | 360 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 57 | |
| 100 to 160 |
| Stiffness to Weight: Axial, points | 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 27 to 75 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 24 to 47 |
| Thermal Shock Resistance, points | 19 to 24 | |
| 23 to 63 |
Alloy Composition
| Carbon (C), % | 0.010 to 0.030 | |
| 2.1 to 2.4 |
| Chromium (Cr), % | 0 | |
| 11 to 13 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.010 | |
| 80.6 to 86.3 |
| Manganese (Mn), % | 0 | |
| 0 to 0.6 |
| Molybdenum (Mo), % | 99.3 to 99.5 | |
| 0.7 to 1.2 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0030 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.4 to 0.55 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 0.060 to 0.12 | |
| 0 |