Grade 364 Molybdenum vs. R30035 Cobalt
Grade 364 molybdenum belongs to the otherwise unclassified metals classification, while R30035 cobalt belongs to the cobalt alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 364 molybdenum and the bottom bar is R30035 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 220 to 230 |
| Elongation at Break, % | 6.2 to 11 | |
| 9.0 to 46 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 120 | |
| 84 to 89 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 720 | |
| 900 to 1900 |
| Tensile Strength: Yield (Proof), MPa | 350 to 620 | |
| 300 to 1650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 320 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 440 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 10 |
| Embodied Energy, MJ/kg | 330 | |
| 140 |
| Embodied Water, L/kg | 360 | |
| 410 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 57 | |
| 160 to 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 630 | |
| 210 to 5920 |
| Stiffness to Weight: Axial, points | 17 | |
| 14 to 15 |
| Stiffness to Weight: Bending, points | 22 | |
| 23 to 24 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 29 to 61 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 24 to 39 |
| Thermal Shock Resistance, points | 19 to 24 | |
| 23 to 46 |
Alloy Composition
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0.010 to 0.040 | |
| 0 to 0.025 |
| Chromium (Cr), % | 0 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 29.1 to 39 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.15 |
| Molybdenum (Mo), % | 99.2 to 99.5 | |
| 9.0 to 10.5 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 33 to 37 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.030 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.15 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0.4 to 0.55 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 0.060 to 0.12 | |
| 0 |