Grade 365 Molybdenum vs. ASTM B596 Au-Cu
Both grade 365 molybdenum and ASTM B596 Au-Cu are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is ASTM B596 Au-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 100 |
| Elongation at Break, % | 6.3 | |
| 4.3 to 17 |
| Poisson's Ratio | 0.31 | |
| 0.41 |
| Shear Modulus, GPa | 120 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 450 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 77 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 150 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 18 |
Common Calculations
| Stiffness to Weight: Axial, points | 17 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 22 | |
| 8.5 |
| Strength to Weight: Axial, points | 17 | |
| 6.8 to 9.4 |
| Strength to Weight: Bending, points | 16 | |
| 7.1 to 8.8 |
| Thermal Shock Resistance, points | 21 | |
| 22 to 30 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 9.0 to 11 |
| Gold (Au), % | 0 | |
| 89 to 91 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 99.9 to 100 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |