Grade 365 Molybdenum vs. Grey Cast Iron

Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while grey cast iron belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is grey cast iron.

Grade 365 Molybdenum Grey Cast Iron

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		180

Elongation at Break, %		6.3
Elongation at Break, %		9.6

Poisson's Ratio		0.31
Poisson's Ratio		0.29

Shear Modulus, GPa		120
Shear Modulus, GPa		69

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		160 to 450

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		98 to 290

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		280

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		490

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		11

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		7.5

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		1.5

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		21

Embodied Water, L/kg		360
Embodied Water, L/kg		44

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		13 to 37

Resilience: Unit (Modulus of Resilience), kJ/m³		450
Resilience: Unit (Modulus of Resilience), kJ/m³		27 to 240

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		5.8 to 17

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		8.7 to 17

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		6.0 to 17

Alloy Composition

Carbon (C), %		0 to 0.010
Carbon (C), %		3.1 to 3.4

Iron (Fe), %		0 to 0.010
Iron (Fe), %		92.1 to 93.9

Manganese (Mn), %		0
Manganese (Mn), %		0.5 to 0.7

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		0

Nickel (Ni), %		0 to 0.0020
Nickel (Ni), %		0

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0015
Oxygen (O), %		0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.9

Silicon (Si), %		0 to 0.010
Silicon (Si), %		2.5 to 2.8

Sulfur (S), %		0
Sulfur (S), %		0 to 0.15