Grade 38 Titanium vs. Solder Alloy 716

Grade 38 titanium belongs to the titanium alloys classification, while solder alloy 716 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 38 titanium and the bottom bar is solder alloy 716.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
51
Elongation at Break, % 11
13
Poisson's Ratio 0.32
0.36
Shear Modulus, GPa 40
19
Tensile Strength: Ultimate (UTS), MPa 1000
39

Thermal Properties

Latent Heat of Fusion, J/g 410
60
Melting Completion (Liquidus), °C 1620
230
Melting Onset (Solidus), °C 1570
220
Specific Heat Capacity, J/kg-K 550
220
Thermal Conductivity, W/m-K 8.0
60
Thermal Expansion, µm/m-K 9.3
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.2
13
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
16

Otherwise Unclassified Properties

Density, g/cm3 4.5
7.3
Embodied Carbon, kg CO2/kg material 35
16
Embodied Energy, MJ/kg 560
270

Common Calculations

Stiffness to Weight: Axial, points 13
3.8
Stiffness to Weight: Bending, points 35
17
Strength to Weight: Axial, points 62
1.5
Strength to Weight: Bending, points 49
3.5
Thermal Diffusivity, mm2/s 3.2
37
Thermal Shock Resistance, points 72
2.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 3.5 to 4.5
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.080
0
Copper (Cu), % 0
0.3 to 0.7
Gold (Au), % 0
0 to 0.050
Hydrogen (H), % 0 to 0.015
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 1.2 to 1.8
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Nickel (Ni), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0.2 to 0.3
0
Silver (Ag), % 0
0.8 to 1.2
Tin (Sn), % 0
97.6 to 98.9
Titanium (Ti), % 89.9 to 93.1
0
Vanadium (V), % 2.0 to 3.0
0
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.4
0