Grade 38 Titanium vs. C68700 Brass
Grade 38 titanium belongs to the titanium alloys classification, while C68700 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is grade 38 titanium and the bottom bar is C68700 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 1000 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 910 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 330 | |
| 160 |
| Melting Completion (Liquidus), °C | 1620 | |
| 970 |
| Melting Onset (Solidus), °C | 1570 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 400 |
| Thermal Conductivity, W/m-K | 8.0 | |
| 100 |
| Thermal Expansion, µm/m-K | 9.3 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.2 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 25 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 26 |
| Density, g/cm3 | 4.5 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 35 | |
| 2.8 |
| Embodied Energy, MJ/kg | 560 | |
| 46 |
| Embodied Water, L/kg | 160 | |
| 340 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3840 | |
| 90 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 35 | |
| 19 |
| Strength to Weight: Axial, points | 62 | |
| 13 |
| Strength to Weight: Bending, points | 49 | |
| 14 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 30 |
| Thermal Shock Resistance, points | 72 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 3.5 to 4.5 | |
| 1.8 to 2.5 |
| Arsenic (As), % | 0 | |
| 0.020 to 0.1 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Copper (Cu), % | 0 | |
| 76 to 79 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 1.2 to 1.8 | |
| 0 to 0.060 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0.2 to 0.3 | |
| 0 |
| Titanium (Ti), % | 89.9 to 93.1 | |
| 0 |
| Vanadium (V), % | 2.0 to 3.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 17.8 to 22.2 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |