Grade 7 Babbitt Metal vs. Commercially Pure Palladium
Both grade 7 Babbitt Metal and commercially pure palladium are otherwise unclassified metals. There are 11 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is commercially pure palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 26 | |
| 120 |
| Poisson's Ratio | 0.4 | |
| 0.39 |
| Shear Modulus, GPa | 9.1 | |
| 43 |
Thermal Properties
| Latent Heat of Fusion, J/g | 48 | |
| 160 |
| Melting Completion (Liquidus), °C | 270 | |
| 1550 |
| Melting Onset (Solidus), °C | 240 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 240 |
| Thermal Expansion, µm/m-K | 26 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 12 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.4 | |
| 5.6 |
| Stiffness to Weight: Bending, points | 9.6 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 14 to 16 | |
| 0 |
| Arsenic (As), % | 0.3 to 0.6 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 |
| Lead (Pb), % | 71.9 to 76.4 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 99.8 to 100 |
| Tin (Sn), % | 9.3 to 10.7 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |