Grade 7 Babbitt Metal vs. Solder Alloy 112
Both grade 7 Babbitt Metal and solder alloy 112 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 60% of their average alloy composition in common. There are 14 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is solder alloy 112.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 26 | |
| 33 |
| Poisson's Ratio | 0.4 | |
| 0.4 |
| Shear Modulus, GPa | 9.1 | |
| 12 |
Thermal Properties
| Latent Heat of Fusion, J/g | 48 | |
| 41 |
| Melting Completion (Liquidus), °C | 270 | |
| 220 |
| Melting Onset (Solidus), °C | 240 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 180 |
| Thermal Expansion, µm/m-K | 26 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 9.4 |
| Embodied Energy, MJ/kg | 62 | |
| 160 |
| Embodied Water, L/kg | 880 | |
| 830 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.4 | |
| 2.0 |
| Stiffness to Weight: Bending, points | 9.6 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 14 to 16 | |
| 0 to 0.050 |
| Arsenic (As), % | 0.3 to 0.6 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 to 0.050 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 to 0.0020 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.020 |
| Lead (Pb), % | 71.9 to 76.4 | |
| 49 to 50.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 9.3 to 10.7 | |
| 49.5 to 50.5 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 to 0.0010 |