MakeItFrom.com
Menu (ESC)

Grade 7 Babbitt Metal vs. SAE-AISI H25 Steel

Grade 7 Babbitt Metal belongs to the otherwise unclassified metals classification, while SAE-AISI H25 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is SAE-AISI H25 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 26
200
Poisson's Ratio 0.4
0.29
Shear Modulus, GPa 9.1
79

Thermal Properties

Latent Heat of Fusion, J/g 48
250
Melting Completion (Liquidus), °C 270
1750
Melting Onset (Solidus), °C 240
1700
Specific Heat Capacity, J/kg-K 150
420
Thermal Expansion, µm/m-K 26
12

Otherwise Unclassified Properties

Base Metal Price, % relative 23
38
Density, g/cm3 10
9.1
Embodied Carbon, kg CO2/kg material 4.4
6.2
Embodied Energy, MJ/kg 62
93
Embodied Water, L/kg 880
83

Common Calculations

Stiffness to Weight: Axial, points 1.4
12
Stiffness to Weight: Bending, points 9.6
22

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 14 to 16
0
Arsenic (As), % 0.3 to 0.6
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.22 to 0.32
Chromium (Cr), % 0
3.8 to 4.5
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 0.1
77.2 to 81.3
Lead (Pb), % 71.9 to 76.4
0
Manganese (Mn), % 0
0.15 to 0.4
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.15 to 0.4
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 9.3 to 10.7
0
Tungsten (W), % 0
14 to 16
Vanadium (V), % 0
0.4 to 0.6
Zinc (Zn), % 0 to 0.0050
0