Grade 702C Zirconium vs. ASTM A182 Grade F10

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while ASTM A182 grade F10 belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is ASTM A182 grade F10.

Grade 702C Cast Zirconium ASTM A182 Grade F10 (S33100) Steel

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness		180
Brinell Hardness		190

Elastic (Young's, Tensile) Modulus, GPa		97
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		13
Elongation at Break, %		34

Poisson's Ratio		0.34
Poisson's Ratio		0.29

Shear Modulus, GPa		36
Shear Modulus, GPa		74

Tensile Strength: Ultimate (UTS), MPa		430
Tensile Strength: Ultimate (UTS), MPa		630

Tensile Strength: Yield (Proof), MPa		310
Tensile Strength: Yield (Proof), MPa		230

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		290

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		5.7
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Density, g/cm³		6.7
Density, g/cm³		7.9

Embodied Water, L/kg		450
Embodied Water, L/kg		120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		52
Resilience: Ultimate (Unit Rupture Work), MJ/m³		170

Resilience: Unit (Modulus of Resilience), kJ/m³		510
Resilience: Unit (Modulus of Resilience), kJ/m³		140

Stiffness to Weight: Axial, points		8.1
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		18
Strength to Weight: Axial, points		22

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		55
Thermal Shock Resistance, points		18

Alloy Composition

Carbon (C), %		0 to 0.1
Carbon (C), %		0.1 to 0.2

Chromium (Cr), %		0
Chromium (Cr), %		7.0 to 9.0

Hafnium (Hf), %		0 to 4.5
Hafnium (Hf), %		0

Hydrogen (H), %		0 to 0.0050
Hydrogen (H), %		0

Iron (Fe), %		0 to 0.3
Iron (Fe), %		66.5 to 72.4

Manganese (Mn), %		0
Manganese (Mn), %		0.5 to 0.8

Nickel (Ni), %		0
Nickel (Ni), %		19 to 22

Nitrogen (N), %		0 to 0.030
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.25
Oxygen (O), %		0

Phosphorus (P), %		0 to 0.010
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0
Silicon (Si), %		1.0 to 1.4

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Zirconium (Zr), %		94.8 to 100
Zirconium (Zr), %		0