Grade 702C Zirconium vs. ASTM A204 Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while ASTM A204 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is ASTM A204 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
18 to 22
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
520 to 590
Tensile Strength: Yield (Proof), MPa 310
290 to 330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 22
52
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
90 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 510
220 to 290
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
18 to 21
Strength to Weight: Bending, points 19
18 to 20
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 55
15 to 17