Grade 702C Zirconium vs. ASTM A369 Grade FP1

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while ASTM A369 grade FP1 belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is ASTM A369 grade FP1.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
20
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
430
Tensile Strength: Yield (Proof), MPa 310
240

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 22
50
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
75
Resilience: Unit (Modulus of Resilience), kJ/m3 510
150
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
15
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 12
13
Thermal Shock Resistance, points 55
13

Alloy Composition

Carbon (C), % 0 to 0.1
0.1 to 0.2
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
97.8 to 99.06
Manganese (Mn), % 0
0.3 to 0.8
Molybdenum (Mo), % 0
0.44 to 0.65
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.025
Silicon (Si), % 0
0.1 to 0.5
Sulfur (S), % 0
0 to 0.025
Zirconium (Zr), % 94.8 to 100
0