Grade 702C Zirconium vs. ASTM Grade LC9 Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while ASTM grade LC9 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is ASTM grade LC9 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
22
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
660
Tensile Strength: Yield (Proof), MPa 310
590

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Specific Heat Capacity, J/kg-K 270
470
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
65

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
140
Resilience: Unit (Modulus of Resilience), kJ/m3 510
920
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
23
Strength to Weight: Bending, points 19
21
Thermal Shock Resistance, points 55
20

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.13
Chromium (Cr), % 0
0 to 0.5
Copper (Cu), % 0
0 to 0.3
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
87.4 to 91.5
Manganese (Mn), % 0
0 to 0.9
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0
8.5 to 10
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0
0 to 0.45
Sulfur (S), % 0
0 to 0.045
Vanadium (V), % 0
0 to 0.030
Zirconium (Zr), % 94.8 to 100
0