Grade 702C Zirconium vs. AWS BAg-5

Both grade 702C zirconium and AWS BAg-5 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is AWS BAg-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
88
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 36
33
Tensile Strength: Ultimate (UTS), MPa 430
150

Thermal Properties

Latent Heat of Fusion, J/g 250
140
Specific Heat Capacity, J/kg-K 270
320
Thermal Expansion, µm/m-K 5.7
21

Otherwise Unclassified Properties

Density, g/cm3 6.7
9.0

Common Calculations

Stiffness to Weight: Axial, points 8.1
5.4
Stiffness to Weight: Bending, points 23
16
Strength to Weight: Axial, points 18
4.6
Strength to Weight: Bending, points 19
6.9
Thermal Shock Resistance, points 55
5.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
29 to 31
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0
Silver (Ag), % 0
44 to 46
Zinc (Zn), % 0
23 to 27
Zirconium (Zr), % 94.8 to 100
0
Residuals, % 0
0 to 0.15