Grade 702C Zirconium vs. AWS BVAg-0

Both grade 702C zirconium and AWS BVAg-0 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is AWS BVAg-0.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
71
Poisson's Ratio 0.34
0.37
Shear Modulus, GPa 36
26
Tensile Strength: Ultimate (UTS), MPa 430
130

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Specific Heat Capacity, J/kg-K 270
240
Thermal Expansion, µm/m-K 5.7
20

Otherwise Unclassified Properties

Density, g/cm3 6.7
10

Common Calculations

Stiffness to Weight: Axial, points 8.1
3.8
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 18
3.4
Strength to Weight: Bending, points 19
5.4
Thermal Shock Resistance, points 55
6.6

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.1
0 to 0.0050
Copper (Cu), % 0
0 to 0.050
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0
Lead (Pb), % 0
0 to 0.0020
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.0020
Silver (Ag), % 0
99.95 to 100
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 94.8 to 100
0