Grade 702C Zirconium vs. EN 1.4031 Stainless Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while EN 1.4031 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is EN 1.4031 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
11 to 13
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 36
76
Tensile Strength: Ultimate (UTS), MPa 430
670 to 900
Tensile Strength: Yield (Proof), MPa 310
390 to 730

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 22
30
Thermal Expansion, µm/m-K 5.7
11

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.7
Embodied Water, L/kg 450
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
77 to 94
Resilience: Unit (Modulus of Resilience), kJ/m3 510
380 to 1360
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 18
24 to 32
Strength to Weight: Bending, points 19
22 to 27
Thermal Diffusivity, mm2/s 12
8.1
Thermal Shock Resistance, points 55
23 to 32

Alloy Composition

Carbon (C), % 0 to 0.1
0.36 to 0.42
Chromium (Cr), % 0
12.5 to 14.5
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
83 to 87.1
Manganese (Mn), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Zirconium (Zr), % 94.8 to 100
0