Grade 702C Zirconium vs. EN 1.4724 Stainless Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while EN 1.4724 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is EN 1.4724 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
16
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 36
75
Tensile Strength: Ultimate (UTS), MPa 430
550
Tensile Strength: Yield (Proof), MPa 310
280

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Specific Heat Capacity, J/kg-K 270
490
Thermal Conductivity, W/m-K 22
21
Thermal Expansion, µm/m-K 5.7
11

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.7
Embodied Water, L/kg 450
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
73
Resilience: Unit (Modulus of Resilience), kJ/m3 510
210
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 12
5.6
Thermal Shock Resistance, points 55
19

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.2
Carbon (C), % 0 to 0.1
0 to 0.12
Chromium (Cr), % 0
12 to 14
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
82.2 to 86.6
Manganese (Mn), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0
0.7 to 1.4
Sulfur (S), % 0
0 to 0.015
Zirconium (Zr), % 94.8 to 100
0