Grade 702C Zirconium vs. EN 1.5805 Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while EN 1.5805 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is EN 1.5805 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 97
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
460 to 1180

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 22
40
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
53

Common Calculations

Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
16 to 42
Strength to Weight: Bending, points 19
17 to 32
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 55
13 to 35

Alloy Composition

Carbon (C), % 0 to 0.1
0.070 to 0.12
Chromium (Cr), % 0
0.9 to 1.2
Copper (Cu), % 0
0 to 0.25
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
95.7 to 97.2
Manganese (Mn), % 0
0.6 to 0.9
Nickel (Ni), % 0
1.2 to 1.5
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.025
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Zirconium (Zr), % 94.8 to 100
0