Grade 702C Zirconium vs. EN 1.7006 Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while EN 1.7006 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is EN 1.7006 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
160 to 220
Elastic (Young's, Tensile) Modulus, GPa 97
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
530 to 1890

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 22
46
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
48

Common Calculations

Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
19 to 67
Strength to Weight: Bending, points 19
19 to 43
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 55
16 to 56

Alloy Composition

Carbon (C), % 0 to 0.1
0.42 to 0.5
Chromium (Cr), % 0
0.4 to 0.6
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
97.6 to 98.7
Manganese (Mn), % 0
0.5 to 0.8
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.035
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0
0 to 0.035
Zirconium (Zr), % 94.8 to 100
0