Grade 702C Zirconium vs. EN 1.7729 Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while EN 1.7729 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is EN 1.7729 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
270
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
17
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
910
Tensile Strength: Yield (Proof), MPa 310
750

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 22
40
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
59

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
150
Resilience: Unit (Modulus of Resilience), kJ/m3 510
1500
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
32
Strength to Weight: Bending, points 19
27
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 55
27

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.080
Arsenic (As), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0 to 0.1
0.17 to 0.23
Chromium (Cr), % 0
0.9 to 1.2
Copper (Cu), % 0
0 to 0.2
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
94.8 to 97
Manganese (Mn), % 0
0.35 to 0.75
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 0
0 to 0.2
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.020
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0
0 to 0.020
Titanium (Ti), % 0
0.070 to 0.15
Vanadium (V), % 0
0.6 to 0.8
Zirconium (Zr), % 94.8 to 100
0