Grade 702C Zirconium vs. EN 2.4680 Cast Nickel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while EN 2.4680 cast nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is EN 2.4680 cast nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
210
Elongation at Break, % 13
9.1
Poisson's Ratio 0.34
0.26
Shear Modulus, GPa 36
84
Tensile Strength: Ultimate (UTS), MPa 430
600
Tensile Strength: Yield (Proof), MPa 310
260

Thermal Properties

Latent Heat of Fusion, J/g 250
350
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 22
14
Thermal Expansion, µm/m-K 5.7
15

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.0
Embodied Water, L/kg 450
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
45
Resilience: Unit (Modulus of Resilience), kJ/m3 510
160
Stiffness to Weight: Axial, points 8.1
15
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 12
3.7
Thermal Shock Resistance, points 55
14

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.1
Chromium (Cr), % 0
48 to 52
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0 to 1.0
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
42.9 to 51
Niobium (Nb), % 0
1.0 to 1.8
Nitrogen (N), % 0 to 0.030
0 to 0.16
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.020
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.020
Zirconium (Zr), % 94.8 to 100
0