Grade 702C Zirconium vs. CR008A Copper

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while CR008A copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is CR008A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
120
Elongation at Break, % 13
15
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 36
43
Tensile Strength: Ultimate (UTS), MPa 430
220
Tensile Strength: Yield (Proof), MPa 310
130

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 22
380
Thermal Expansion, µm/m-K 5.7
17

Otherwise Unclassified Properties

Density, g/cm3 6.7
9.0
Embodied Water, L/kg 450
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
29
Resilience: Unit (Modulus of Resilience), kJ/m3 510
76
Stiffness to Weight: Axial, points 8.1
7.2
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 18
6.8
Strength to Weight: Bending, points 19
9.0
Thermal Diffusivity, mm2/s 12
110
Thermal Shock Resistance, points 55
7.8

Alloy Composition

Bismuth (Bi), % 0
0 to 0.00050
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
99.95 to 100
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0
Lead (Pb), % 0
0 to 0.0050
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0
Silver (Ag), % 0
0 to 0.015
Zirconium (Zr), % 94.8 to 100
0