Grade 702C Zirconium vs. Grade 1 Babbitt Metal

Both grade 702C zirconium and grade 1 Babbitt Metal are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is grade 1 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
13
Elastic (Young's, Tensile) Modulus, GPa 97
53
Elongation at Break, % 13
34
Poisson's Ratio 0.34
0.35
Shear Modulus, GPa 36
20
Tensile Strength: Yield (Proof), MPa 310
30

Thermal Properties

Latent Heat of Fusion, J/g 250
70
Specific Heat Capacity, J/kg-K 270
230
Thermal Conductivity, W/m-K 22
45
Thermal Expansion, µm/m-K 5.7
21

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.3
Embodied Water, L/kg 450
1160

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 510
8.6
Stiffness to Weight: Axial, points 8.1
4.0
Stiffness to Weight: Bending, points 23
17
Thermal Diffusivity, mm2/s 12
26

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
4.0 to 5.0
Arsenic (As), % 0
0 to 0.1
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
4.0 to 5.0
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0 to 0.080
Lead (Pb), % 0
0 to 0.35
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0
Tin (Sn), % 0
89.3 to 92
Zinc (Zn), % 0
0 to 0.0050
Zirconium (Zr), % 94.8 to 100
0