Grade 702C Zirconium vs. Grade CW2M Nickel
Grade 702C zirconium belongs to the otherwise unclassified metals classification, while grade CW2M nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 702C zirconium and the bottom bar is grade CW2M nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 210 |
| Elongation at Break, % | 13 | |
| 23 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 36 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 560 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 330 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 430 |
| Thermal Expansion, µm/m-K | 5.7 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 8.8 |
| Embodied Water, L/kg | 450 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 52 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 | |
| 220 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 18 | |
| 18 |
| Strength to Weight: Bending, points | 19 | |
| 17 |
| Thermal Shock Resistance, points | 55 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 | |
| 15 to 17.5 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 15 to 17.5 |
| Nickel (Ni), % | 0 | |
| 60.1 to 70 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 94.8 to 100 | |
| 0 |