Grade 702C Zirconium vs. Grade M35-2 Nickel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while grade M35-2 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is grade M35-2 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
160
Elongation at Break, % 13
28
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 36
62
Tensile Strength: Ultimate (UTS), MPa 430
500
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Specific Heat Capacity, J/kg-K 270
430
Thermal Conductivity, W/m-K 22
22
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.8
Embodied Water, L/kg 450
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
120
Resilience: Unit (Modulus of Resilience), kJ/m3 510
170
Stiffness to Weight: Axial, points 8.1
10
Stiffness to Weight: Bending, points 23
21
Strength to Weight: Axial, points 18
16
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 12
5.7
Thermal Shock Resistance, points 55
17

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.35
Copper (Cu), % 0
26 to 33
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0 to 3.5
Manganese (Mn), % 0
0 to 1.5
Nickel (Ni), % 0
59.1 to 74
Niobium (Nb), % 0
0 to 0.5
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.030
Silicon (Si), % 0
0 to 2.0
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 94.8 to 100
0