Grade 702C Zirconium vs. Grade N7M Nickel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while grade N7M nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is grade N7M nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
220
Elongation at Break, % 13
22
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 36
85
Tensile Strength: Ultimate (UTS), MPa 430
590
Tensile Strength: Yield (Proof), MPa 310
310

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Specific Heat Capacity, J/kg-K 270
390
Thermal Expansion, µm/m-K 5.7
9.9

Otherwise Unclassified Properties

Density, g/cm3 6.7
9.3
Embodied Water, L/kg 450
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
110
Resilience: Unit (Modulus of Resilience), kJ/m3 510
220
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 18
18
Strength to Weight: Bending, points 19
17
Thermal Shock Resistance, points 55
19

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.070
Chromium (Cr), % 0
0 to 1.0
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0 to 3.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
30 to 33
Nickel (Ni), % 0
60.9 to 70
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 94.8 to 100
0