Grade 702C Zirconium vs. Solder Alloy 503

Both grade 702C zirconium and solder alloy 503 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is solder alloy 503.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
54
Elongation at Break, % 13
30
Poisson's Ratio 0.34
0.36
Shear Modulus, GPa 36
20
Tensile Strength: Ultimate (UTS), MPa 430
57

Thermal Properties

Latent Heat of Fusion, J/g 250
69
Specific Heat Capacity, J/kg-K 270
230
Thermal Conductivity, W/m-K 22
61
Thermal Expansion, µm/m-K 5.7
22

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.5

Common Calculations

Stiffness to Weight: Axial, points 8.1
4.1
Stiffness to Weight: Bending, points 23
17
Strength to Weight: Axial, points 18
2.1
Strength to Weight: Bending, points 19
4.4
Thermal Diffusivity, mm2/s 12
35
Thermal Shock Resistance, points 55
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
5.5 to 6.5
Gold (Au), % 0
0 to 0.050
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.3
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Nickel (Ni), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0
Silver (Ag), % 0
1.8 to 2.2
Tin (Sn), % 0
90.8 to 92.7
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 94.8 to 100
0