Grade 702C Zirconium vs. SAE-AISI 8740 Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while SAE-AISI 8740 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is SAE-AISI 8740 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170 to 200
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
11 to 23
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
73
Tensile Strength: Ultimate (UTS), MPa 430
580 to 670
Tensile Strength: Yield (Proof), MPa 310
380 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 22
39
Thermal Expansion, µm/m-K 5.7
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
71 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 510
390 to 850
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 18
20 to 24
Strength to Weight: Bending, points 19
20 to 22
Thermal Diffusivity, mm2/s 12
10
Thermal Shock Resistance, points 55
17 to 20

Alloy Composition

Carbon (C), % 0 to 0.1
0.38 to 0.43
Chromium (Cr), % 0
0.4 to 0.6
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
96.5 to 97.7
Manganese (Mn), % 0
0.75 to 1.0
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0
0.4 to 0.7
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Zirconium (Zr), % 94.8 to 100
0