Grade 702C Zirconium vs. C17200 Copper

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while C17200 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is C17200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
120
Elongation at Break, % 13
1.1 to 37
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 36
45
Tensile Strength: Ultimate (UTS), MPa 430
480 to 1380
Tensile Strength: Yield (Proof), MPa 310
160 to 1250

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 22
110
Thermal Expansion, µm/m-K 5.7
18

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.8
Embodied Water, L/kg 450
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
4.2 to 500
Resilience: Unit (Modulus of Resilience), kJ/m3 510
110 to 5720
Stiffness to Weight: Axial, points 8.1
7.6
Stiffness to Weight: Bending, points 23
19
Strength to Weight: Axial, points 18
15 to 44
Strength to Weight: Bending, points 19
16 to 31
Thermal Diffusivity, mm2/s 12
31
Thermal Shock Resistance, points 55
16 to 46

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.2
Beryllium (Be), % 0
1.8 to 2.0
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
96.1 to 98
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0 to 0.4
Nickel (Ni), % 0
0.2 to 0.6
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0
0 to 0.2
Zirconium (Zr), % 94.8 to 100
0
Residuals, % 0
0 to 0.5