Grade 702C Zirconium vs. C19800 Copper

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while C19800 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is C19800 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
110
Elongation at Break, % 13
9.0 to 12
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 36
43
Tensile Strength: Ultimate (UTS), MPa 430
430 to 550
Tensile Strength: Yield (Proof), MPa 310
420 to 550

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 22
260
Thermal Expansion, µm/m-K 5.7
18

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.9
Embodied Water, L/kg 450
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
49 to 52
Resilience: Unit (Modulus of Resilience), kJ/m3 510
770 to 1320
Stiffness to Weight: Axial, points 8.1
7.2
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 18
14 to 17
Strength to Weight: Bending, points 19
14 to 17
Thermal Diffusivity, mm2/s 12
75
Thermal Shock Resistance, points 55
15 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
95.7 to 99.47
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0.020 to 0.5
Magnesium (Mg), % 0
0.1 to 1.0
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0.010 to 0.1
Tin (Sn), % 0
0.1 to 1.0
Zinc (Zn), % 0
0.3 to 1.5
Zirconium (Zr), % 94.8 to 100
0
Residuals, % 0
0 to 0.2