Grade 702C Zirconium vs. C65100 Bronze

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while C65100 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is C65100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
120
Elongation at Break, % 13
2.4 to 50
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 36
43
Tensile Strength: Ultimate (UTS), MPa 430
280 to 560
Tensile Strength: Yield (Proof), MPa 310
95 to 440

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 22
57
Thermal Expansion, µm/m-K 5.7
18

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.8
Embodied Water, L/kg 450
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
12 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 510
39 to 820
Stiffness to Weight: Axial, points 8.1
7.3
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 18
8.7 to 18
Strength to Weight: Bending, points 19
11 to 17
Thermal Diffusivity, mm2/s 12
16
Thermal Shock Resistance, points 55
9.5 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
94.5 to 99.2
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0 to 0.8
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.7
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0
0.8 to 2.0
Zinc (Zn), % 0
0 to 1.5
Zirconium (Zr), % 94.8 to 100
0
Residuals, % 0
0 to 0.5