Grade 702C Zirconium vs. C71640 Copper-nickel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while C71640 copper-nickel belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is C71640 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
140
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 36
52
Tensile Strength: Ultimate (UTS), MPa 430
490 to 630
Tensile Strength: Yield (Proof), MPa 310
190 to 460

Thermal Properties

Latent Heat of Fusion, J/g 250
240
Specific Heat Capacity, J/kg-K 270
410
Thermal Conductivity, W/m-K 22
29
Thermal Expansion, µm/m-K 5.7
15

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.9
Embodied Water, L/kg 450
280

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 510
130 to 750
Stiffness to Weight: Axial, points 8.1
8.7
Stiffness to Weight: Bending, points 23
20
Strength to Weight: Axial, points 18
15 to 20
Strength to Weight: Bending, points 19
16 to 18
Thermal Diffusivity, mm2/s 12
8.2
Thermal Shock Resistance, points 55
16 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
61.7 to 67.8
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
1.7 to 2.3
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0
1.5 to 2.5
Nickel (Ni), % 0
29 to 32
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0
Zinc (Zn), % 0
0 to 1.0
Zirconium (Zr), % 94.8 to 100
0
Residuals, % 0
0 to 0.5