Grade 702C Zirconium vs. S36200 Stainless Steel

Grade 702C zirconium belongs to the otherwise unclassified metals classification, while S36200 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is grade 702C zirconium and the bottom bar is S36200 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 13
3.4 to 4.6
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 36
76
Tensile Strength: Ultimate (UTS), MPa 430
1180 to 1410
Tensile Strength: Yield (Proof), MPa 310
960 to 1240

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 22
16
Thermal Expansion, µm/m-K 5.7
11

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 450
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
46 to 51
Resilience: Unit (Modulus of Resilience), kJ/m3 510
2380 to 3930
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 18
42 to 50
Strength to Weight: Bending, points 19
32 to 36
Thermal Diffusivity, mm2/s 12
4.3
Thermal Shock Resistance, points 55
40 to 48

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0 to 0.1
0 to 0.050
Chromium (Cr), % 0
14 to 14.5
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
75.4 to 79.5
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
0 to 0.3
Nickel (Ni), % 0
6.5 to 7.0
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.010
0 to 0.030
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0
0.6 to 0.9
Zirconium (Zr), % 94.8 to 100
0