Grade 704C Zirconium vs. ASTM A182 Grade F5a

Grade 704C zirconium belongs to the otherwise unclassified metals classification, while ASTM A182 grade F5a belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is ASTM A182 grade F5a.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
310
Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 11
25
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
74
Tensile Strength: Ultimate (UTS), MPa 470
710
Tensile Strength: Yield (Proof), MPa 310
520

Thermal Properties

Latent Heat of Fusion, J/g 240
260
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 21
40
Thermal Expansion, µm/m-K 5.9
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 460
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 48
160
Resilience: Unit (Modulus of Resilience), kJ/m3 490
700
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 58
20

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.25
Chromium (Cr), % 0
4.0 to 6.0
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
91.4 to 95.6
Manganese (Mn), % 0
0 to 0.6
Molybdenum (Mo), % 0
0.44 to 0.65
Nickel (Ni), % 0
0 to 0.5
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.0 to 2.0
0
Zirconium (Zr), % 92.9 to 99
0