Grade 704C Zirconium vs. AWS E310Mo

Grade 704C zirconium belongs to the otherwise unclassified metals classification, while AWS E310Mo belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is AWS E310Mo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
200
Elongation at Break, % 11
34
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 36
80
Tensile Strength: Ultimate (UTS), MPa 470
620

Thermal Properties

Latent Heat of Fusion, J/g 240
310
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 21
14
Thermal Expansion, µm/m-K 5.9
14

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 460
210

Common Calculations

Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 12
3.7
Thermal Shock Resistance, points 58
15

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.12
Chromium (Cr), % 0
25 to 28
Copper (Cu), % 0
0 to 0.75
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
42.8 to 52
Manganese (Mn), % 0
1.0 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
20 to 22
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0 to 0.030
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.0 to 2.0
0
Zirconium (Zr), % 92.9 to 99
0