Grade 704C Zirconium vs. AWS E410

Grade 704C zirconium belongs to the otherwise unclassified metals classification, while AWS E410 belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is AWS E410.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
190
Elongation at Break, % 11
23
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 36
76
Tensile Strength: Ultimate (UTS), MPa 470
580
Tensile Strength: Yield (Proof), MPa 310
440

Thermal Properties

Latent Heat of Fusion, J/g 240
270
Specific Heat Capacity, J/kg-K 270
480
Thermal Conductivity, W/m-K 21
28
Thermal Expansion, µm/m-K 5.9
14

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 460
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 48
120
Resilience: Unit (Modulus of Resilience), kJ/m3 490
500
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 12
7.5
Thermal Shock Resistance, points 58
16

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.12
Chromium (Cr), % 0
11 to 13.5
Copper (Cu), % 0
0 to 0.75
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
82.2 to 89
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0
0 to 0.7
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0
0 to 0.9
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.0 to 2.0
0
Zirconium (Zr), % 92.9 to 99
0