Grade 704C Zirconium vs. EN 1.1172 Steel

Grade 704C zirconium belongs to the otherwise unclassified metals classification, while EN 1.1172 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is EN 1.1172 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 97
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 36
72
Tensile Strength: Ultimate (UTS), MPa 470
480 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 240
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 21
51
Thermal Expansion, µm/m-K 5.9
12

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.8
Embodied Water, L/kg 460
46

Common Calculations

Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 20
17 to 61
Strength to Weight: Bending, points 20
17 to 41
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 58
15 to 55

Alloy Composition

Carbon (C), % 0 to 0.1
0.32 to 0.39
Copper (Cu), % 0
0 to 0.25
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
98.2 to 99.18
Manganese (Mn), % 0
0.5 to 0.8
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0 to 0.025
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 1.0 to 2.0
0
Zirconium (Zr), % 92.9 to 99
0