Grade 704C Zirconium vs. CR007A Copper

Grade 704C zirconium belongs to the otherwise unclassified metals classification, while CR007A copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is CR007A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
120
Elongation at Break, % 11
15
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 36
43
Tensile Strength: Ultimate (UTS), MPa 470
230
Tensile Strength: Yield (Proof), MPa 310
140

Thermal Properties

Latent Heat of Fusion, J/g 240
210
Specific Heat Capacity, J/kg-K 270
390
Thermal Conductivity, W/m-K 21
380
Thermal Expansion, µm/m-K 5.9
17

Otherwise Unclassified Properties

Density, g/cm3 6.7
9.0
Embodied Water, L/kg 460
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 48
31
Resilience: Unit (Modulus of Resilience), kJ/m3 490
83
Stiffness to Weight: Axial, points 8.1
7.2
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 20
7.1
Strength to Weight: Bending, points 20
9.3
Thermal Diffusivity, mm2/s 12
110
Thermal Shock Resistance, points 58
8.1

Alloy Composition

Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
99.994 to 100
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.3
0 to 0.0010
Lead (Pb), % 0
0 to 0.00050
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0
Selenium (Se), % 0
0 to 0.00020
Silver (Ag), % 0
0 to 0.0025
Sulfur (S), % 0
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020
Tin (Sn), % 1.0 to 2.0
0
Zirconium (Zr), % 92.9 to 99
0