Grade 704C Zirconium vs. Grade 20 Titanium
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while grade 20 titanium belongs to the titanium alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is grade 20 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 120 |
| Elongation at Break, % | 11 | |
| 5.7 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 36 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 900 to 1270 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 850 to 1190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 520 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 5.0 |
| Embodied Water, L/kg | 460 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 71 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 2940 to 5760 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 33 |
| Strength to Weight: Axial, points | 20 | |
| 50 to 70 |
| Strength to Weight: Bending, points | 20 | |
| 41 to 52 |
| Thermal Shock Resistance, points | 58 | |
| 55 to 77 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 5.5 to 6.5 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 to 0.12 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 71 to 77 |
| Vanadium (V), % | 0 | |
| 7.5 to 8.5 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |