Grade 704C Zirconium vs. Solder Alloy 142

Both grade 704C zirconium and solder alloy 142 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is solder alloy 142.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 97
33
Elongation at Break, % 11
37
Poisson's Ratio 0.34
0.4
Shear Modulus, GPa 36
12
Tensile Strength: Ultimate (UTS), MPa 470
43

Thermal Properties

Latent Heat of Fusion, J/g 240
42
Specific Heat Capacity, J/kg-K 270
170
Thermal Conductivity, W/m-K 21
45
Thermal Expansion, µm/m-K 5.9
25

Otherwise Unclassified Properties

Density, g/cm3 6.7
9.3
Embodied Water, L/kg 460
890

Common Calculations

Stiffness to Weight: Axial, points 8.1
2.0
Stiffness to Weight: Bending, points 23
11
Strength to Weight: Axial, points 20
1.3
Strength to Weight: Bending, points 20
2.9
Thermal Diffusivity, mm2/s 12
28
Thermal Shock Resistance, points 58
3.7

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
2.5 to 3.5
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.3
0 to 0.020
Lead (Pb), % 0
47.4 to 50
Nickel (Ni), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 1.0 to 2.0
47.5 to 48.5
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 92.9 to 99
0