Grade 705C Zirconium vs. S17700 Stainless Steel
Grade 705C zirconium belongs to the otherwise unclassified metals classification, while S17700 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 705C zirconium and the bottom bar is S17700 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 | |
| 180 to 430 |
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 200 |
| Elongation at Break, % | 13 | |
| 1.0 to 23 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 36 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 1180 to 1650 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 430 to 1210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 480 |
| Thermal Conductivity, W/m-K | 18 | |
| 15 |
| Thermal Expansion, µm/m-K | 5.7 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.7 |
| Embodied Water, L/kg | 450 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 66 | |
| 15 to 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 790 | |
| 460 to 3750 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 22 | |
| 42 to 59 |
| Strength to Weight: Bending, points | 22 | |
| 32 to 40 |
| Thermal Diffusivity, mm2/s | 9.9 | |
| 4.1 |
| Thermal Shock Resistance, points | 69 | |
| 39 to 54 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.75 to 1.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.090 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 70.5 to 76.8 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 6.5 to 7.8 |
| Niobium (Nb), % | 2.0 to 3.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zirconium (Zr), % | 91.9 to 98 | |
| 0 |