Grade 8 Babbitt Metal vs. ASTM A732 Cast Steel
Grade 8 Babbitt Metal belongs to the otherwise unclassified metals classification, while ASTM A732 cast steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 8 Babbitt Metal and the bottom bar is ASTM A732 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 15 | |
| 140 to 440 |
| Elastic (Young's, Tensile) Modulus, GPa | 24 | |
| 190 |
| Poisson's Ratio | 0.41 | |
| 0.29 |
| Shear Modulus, GPa | 8.5 | |
| 72 to 73 |
| Tensile Strength: Yield (Proof), MPa | 23 | |
| 310 to 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 46 | |
| 250 to 260 |
| Melting Completion (Liquidus), °C | 270 | |
| 1440 to 1460 |
| Melting Onset (Solidus), °C | 240 | |
| 1400 to 1420 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 470 to 480 |
| Thermal Conductivity, W/m-K | 24 | |
| 39 to 50 |
| Thermal Expansion, µm/m-K | 24 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 2.0 to 3.8 |
| Density, g/cm3 | 10 | |
| 7.8 to 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 1.4 to 1.7 |
| Embodied Energy, MJ/kg | 53 | |
| 19 to 24 |
| Embodied Water, L/kg | 840 | |
| 47 to 54 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 11 | |
| 260 to 4770 |
| Stiffness to Weight: Axial, points | 1.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 9.2 | |
| 24 |
| Thermal Diffusivity, mm2/s | 16 | |
| 10 to 14 |