Grade CU5MCuC Nickel vs. C47940 Brass
Grade CU5MCuC nickel belongs to the nickel alloys classification, while C47940 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is grade CU5MCuC nickel and the bottom bar is C47940 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 22 | |
| 14 to 34 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 380 to 520 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 160 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 130 |
| Melting Completion (Liquidus), °C | 1420 | |
| 850 |
| Melting Onset (Solidus), °C | 1370 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 25 |
| Density, g/cm3 | 8.2 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 110 | |
| 47 |
| Embodied Water, L/kg | 230 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 68 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
| 120 to 740 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 20 | |
| 13 to 17 |
| Strength to Weight: Bending, points | 19 | |
| 14 to 17 |
| Thermal Shock Resistance, points | 16 | |
| 13 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 19.5 to 23.5 | |
| 0 |
| Copper (Cu), % | 1.5 to 3.5 | |
| 63 to 66 |
| Iron (Fe), % | 22.2 to 37.9 | |
| 0.1 to 1.0 |
| Lead (Pb), % | 0 | |
| 1.0 to 2.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 0 |
| Nickel (Ni), % | 38 to 44 | |
| 0.1 to 0.5 |
| Niobium (Nb), % | 0.6 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.2 to 2.0 |
| Zinc (Zn), % | 0 | |
| 28.1 to 34.6 |
| Residuals, % | 0 | |
| 0 to 0.4 |