Grade CW12MW Nickel vs. CC330G Bronze

Grade CW12MW nickel belongs to the nickel alloys classification, while CC330G bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is grade CW12MW nickel and the bottom bar is CC330G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
110
Elongation at Break, % 4.6
20
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 85
42
Tensile Strength: Ultimate (UTS), MPa 560
530
Tensile Strength: Yield (Proof), MPa 310
190

Thermal Properties

Latent Heat of Fusion, J/g 320
230
Maximum Temperature: Mechanical, °C 960
220
Melting Completion (Liquidus), °C 1610
1050
Melting Onset (Solidus), °C 1560
1000
Specific Heat Capacity, J/kg-K 410
430
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 70
29
Density, g/cm3 9.1
8.4
Embodied Carbon, kg CO2/kg material 13
3.2
Embodied Energy, MJ/kg 180
52
Embodied Water, L/kg 280
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
82
Resilience: Unit (Modulus of Resilience), kJ/m3 220
170
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 22
19
Strength to Weight: Axial, points 17
18
Strength to Weight: Bending, points 17
17
Thermal Shock Resistance, points 16
19

Alloy Composition

Aluminum (Al), % 0
8.0 to 10.5
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 15.5 to 17.5
0
Copper (Cu), % 0
87 to 92
Iron (Fe), % 4.5 to 7.5
0 to 1.2
Lead (Pb), % 0
0 to 0.3
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 16 to 18
0
Nickel (Ni), % 49.2 to 60.1
0 to 1.0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.2
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.3
Tungsten (W), % 3.8 to 5.3
0
Vanadium (V), % 0.2 to 0.4
0
Zinc (Zn), % 0
0 to 0.5